Double layer structural effects in the copper electrodeposition kinetics studied by Faradaic impedance and quartz microbalance methods.

Соловьева Т.Г., Никифорова Т.Г., Малев В.В.
Эффекты строения двойного электрического слоя в кинетике электроосаждения меди, исследовавшейся методами фарадеевского импеданса и кварцевой гравиметрии.

Russia / Россия

Impedance measurements under the copper electrodeposition revealed significant differences in parameters of the electrode processes proceeding in sulfate and perchlorate solutions. This made it possible to suggest that, at least in the case of sulfate solutions, there might proceed anion adsorption at the positively charged copper electrode. This suggestion about the possible influence of the double layer structure on the kinetics of studied processes was confirmed in result of subsequent microbalance measurements.

Измерения импеданса при электроосаждении меди выявили значительное различие параметров электродных процессов, протекающих в сульфатных и перхлоратных электролитах. Это позволило предположить, что, по крайней мере, в случае сульфатных электролитов протекает адсорбция анионов на положительно заряженной поверхности электрода. Предположение о возможном влиянии строения двойного слоя на кинетику исследуемых процессов было подтверждено в ходе последующих измерений методом кварцевой гравиметрии.