Vitjunin M.A., Chikova O.A., Chentsov V.P., Pastukhov E.A.
The aluminium based melts spreading kinetics upon St3 steel surface.

Витюнин М.А., Чикова О.А., Ченцов В.П., Пастухов Э.А.
Кинетика растекания расплавов на основе алюминия по стали Ст3.

Russia / Россия

The temperature and time dependences of contact angle and the diameter of spreading drop of AL852, AL5M, AL9, 7075 melts on the steel (St3) were measured by the method of the sessile drop. The melts AL9, 7075, AL5M were found to wet the steel surface at 900 °C and the melt A852 at 800 C; the intensive spreading of all investigated melts takes place at 1000 °C. The temperature of the transition from nonwetting to wetting is correlated with the stability of oxide film on the surface of aluminum melt.

Методом лежащей капли измерены температурные и временные зависимости угла смачивания и диаметра пятна растекания расплавов АЛ852, АЛ5М, АЛ9, 7075 по стали Ст3. Расплавы АЛ9, 7075, АЛ5М смачивают поверхности стали Ст3 при температуре 900 °С, расплав А852 — при температуре 800 °С; интенсивное растекание жидкого металла для всех изученных композиций происходит при 1000 °С. Температура перехода от несмачивания к смачиванию коррелирует с термодинамической стабильностью оксидной плёнки на поверхности алюминиевого расплава.