GP29

Tolochko B.P., Chernyshev A.P., Ten K.A., Zubkov P.I., Lyakhov N.Z.
Features of detonation synthesis of alloy nanoparticles from metal carboxylates.

Толочко Б.П., Чернышев А.П., Тен К.А., Зубков П.И., Ляхов Н.З.
Особенности детонационного синтеза наночастиц сплавов из карбоксилатов металлов.

Russia / Россия

We have ascertained that a shock wave impact on solid solutions of metal stearates results in formation of alloy nanoparticles that consist of a nucleus and carbon shell. The typical dimensions of PbBi alloy nanoparticles obtained from a solid solution of lead stearate and bismuth stearate were 5 to 50 nm. The molar ratio of stearates in the solid solution was 1 : 1. The solid solution was powdered to ~ 10 μm and mixed with ten. The charge mass was about 15 grams. The charge was blasted in helium in a 0,113 m3 blasting chamber.

Установлено, что при воздействии ударной волны на твердые растворы стеаратов металлов образуются наночастицы сплавов, состоящие из образованного сплавом ядра и углеродной оболочки. Характерные размеры наночастиц сплава PbBi, полученных из твердого раствора стеарата свинца и стеарата висмута, составляли 5—50 нм. Твердый раствор измельчали до размера ~ 10 мкм и смешивали с тэном. Масса составляла около 15 г. Подрыв производился во взрывной камере объемом 0.113 м3; в атмосфере гелия.